Angelus Bio-C Sealer - BioCeramic Root Canal Sealer

Angelus Bio C Sealer - Bioceramic root canal sealer

Introduction

• Bio-C Sealer is a ready-to-use bioceramic sealer for root canal filling.
• The bioceramic composition allows the release of calcium ions, which stimulates the formation of mineralized tissue.
• Its mechanical and physical properties make it easy to manipulate and seal the canals, and its biological properties and high pH confer safety and treatment success

Flow

• High flowability allows the filling of the main and accessory canal easily.
• The smooth flow ensures that the filling are complete and sturdy

Radiopacity

• BIO-C® SEALER presents high opacity ( ≥ 7 mm of the Aluminium step-wedge), providing an excellent radiographic view.

Setting time

• Bio-C Sealer setting reaction occurs through the contact with the moisture from dentinal canaliculi and periapical tissues, as it is a product with hydraulic characteristics.
• Setting occurs between 60 and 120 minutes.
• The setting time ensures that it is accurate, and provides a longer lasting restoration

Film thickness

• Particle size of less than 2 μm provides thin (> 50 μm) thickness.
• The thinness allows the complete settling of gutta-percha, as well as cement penetration into the dentinal tubules.

Particle size

• Particle size (less than 2 μm) provides Bio-C Sealer with excellent flow, thin film thickness and diffusion to tissues, leading to a faster regeneration.

Release of calcium ions

• The release of Calcium ions is fundamental for the biological and chemical action of a filling cement.
• Bio-C Sealer presents constant release of Calcium to the tissues
• Our product helps in promoting biomineralization and stimulation of the tissues for their fast regeneration

Antibacterial action

• The high pH (12.5) gives Bio-C Sealer an antibacterial action, desirable for endodontic cements,
• The results and treatment prognosis thus provided are favorable and a step in the right direction.

Characteristics and benefits

• Pre-mixed: Ready for use/injectable;
• With Zirconia Oxide: Does not cause staining;
• Bioceramic formulation: High biocompatibility;
• Release of Calcium ions: Bioactivity;
• Alkaline: Antibacterial action;
• Interaction with dentin: High adhesion
• Bio-C Sealer is a non-resin cement that, in addition to its improved biocompatibility properties, also provides an easy pulp chamber cleaning after endodontic obturation.
• EUGENOL FREE: Bio-C Sealer is free of Eugenol and therefore has lower cytotoxicity, does not cause staining and does not interfere with the polymerization of resinous materials (resin cements and composite resins)

Technical Details

Setting Time: 120- 240 mins
Radiopacity: > 70 mm AI
pH: -12
Flow: 23.46 mm
Size of Particules: < 2 um
Film Thickness: 21 um
Solubility: 2.86%
Resistance to Compression: 9.72 + 2.48 MPa